Carbon Steel Pipe Reducing Tee
Metleader inc provides you with Carbon Steel Pipe Reducing Tee of a variety specifications and standards.The branch tube is different from the other two diameters and is called pipe reducing tee. For pipe reducing tee carbon steel, such as "T4x4x3.5", the same diameter of four-inch diameter of 3.5-inch reducing tee.
Standards: ANSI B16.9, ASME, MSS SP, DIN, GOST, JIS2220, EN
Sch5s, Sch10s, Sch10, Sch20, Sch30, Sch40s, STD, Sch40, Sch60, Sch80s, XS, Sch80, Sch100, Sch120, Sch140, Sch160, XXS
Seamless elbow: 1/2"～36" DN15～DN900
Welding elbow: 6"～72" DN150～DN1800
Carbon Steel: ASTM A105, A234 WPB, WPHY 42, 46, 52, 56, 60, 65, 70, 80
Stainless steel: ASTM/ASME A403 WP 304, 304L, 316, 316l
Alloy Steel: ASTM A234 WP1, WP5, WP9, WP11, WP22, WP91
Low Temperature Steel: ASTM A420 WPL 1, WPL 3, WPL 6
Production process of Carbon Steel Pipe Reducing Tee:
There are two ways to forming
- 1 Hydraulic bulge shape
The hydraulic bulging of tee is a kind of forming process which is compensated by the axial compensation of the metal material. The process is to use a special hydraulic machine, will be equal to the tee diameter of the tube injected into the liquid, by synchronizing the two horizontal cylinders of the hydraulic press with the medium motion extruded tube Billet, the volume becomes smaller after extrusion, and the liquid in the Tube billet increases with the volume of the tube, and when the pressure of the tee branch tube expands, Metal material in the side cylinder and tube billet under the dual action of the liquid pressure in the mold cavity flow and swell out of the branch tube.
Due to the seamless tee hydraulic bulging process requires the large tonnage of equipment, is currently used mainly less than DN400 standard wall thickness tee manufacturing.
- 2 Hot forming
The tee hot-pressing forming is a tube billet larger than the tee diameter, flattening about the size of the tee diameter.It is a commonly used production technology of partial large diameter tee.